ASME Section IX Quiz/10 5 votes, 4.8 avg 331 Created on March 09, 2023ASME Section IX Quiz-1ASME Section IX quiz one should take before interview 1 / 10Guided-bend specimens shall have no open defects in the weld or heat effected zone exceeding __________ measured in any direction on the convex surface of the specimen after bending. 2mm 3mm 5mm 4mm 2 / 10The PQR must list: Essential variables Qualification test & examination results Supplementary essential variables (when notch toughness is required) All of the Above None of the Above 3 / 10What is the earliest Edition of Section IX recognized by the current edition? 1958 1992 1987 1962 None of the Above 4 / 10A welder qualifying with a groove weld welded from both sides is qualified to weld ________________ Without backing With , Without Backing With backing only None of the Above 5 / 10When a tensile specimen breaks in the base metal outside of the weld or fusion line, the strength recorded may be at most ____ below the specified tensile and be accepted. 3.5% 0.5% 5% All of the above 6 / 10Charpy V-notch tests are performed to determine a weldment’s Tensile strength Ductility Notch toughness All of above B and C both 7 / 10A welder qualifying by making a groove weld on pipe with an O.D. of 26.1 in the 5G position is qualified to weld groove welds in 25mm O.D. Pipe in the overhead position 21.3mm O.D. Pipe in the vertical position 168.3 O.D. pipe in the horizontal position 25mm O.D. Pipe in the horizontal position All of the above 8 / 10The basic purpose of testing a welder is to establish the welder’s Knowledge of welding requirements Ability to deposit sound weld metal Mechanical ability to operate equipment General attitude toward welding inspectors None of the above 9 / 10A welder is qualified welding in 5G position is qualified for what position on plate ? F, H, OH F, V, OH V, OH, SP H, V, OH 10 / 10A welder qualifying with a groove weld in plate in the 4G position is qualified to weld groove welds in plate and pipe over 24”O.D. in at least the A. Vertical Flat & horizontal Flat & overhead Horizontal Your score is LinkedIn Facebook VKontakte 0% Restart quiz Please rate this quiz Send feedback /10 0 votes, 0 avg 2 Created on March 09, 2023ASME Section IX Quiz-2ASME Section IX quiz one should take before interview 1 / 10Immediate retests of welders’ qualifications coupons: Must use the same method May use any method Are not allowed Require Inspector approval 2 / 10Which of the following welding processes are currently not permitted to be used with SWPs as referenced in Appendix E of ASME IX? GMAW SAW PAW All of the above 3 / 10A welder qualified for SMAW using an E7018 electrode is also qualified to weld with: E7015 E6011 E6010 E7024 All of the Above 4 / 10A welder qualified to weld in the 2G position on pipe would have to be qualified in which of the additional positions to qualify for all position groove welding on pipe? 1G 2G 5G 4G All of the above 5 / 10Reduced-section tensile test specimens conforming to QW-462.1 (b) may be used on all thicknesses of pipe having an outside diameter greater than: 2 inches 2 .5 inches 3 inches 3.5 Inches 4 Inches 6 / 10When using radiographs to qualify welder, the acceptance standards used are found in ASME Section V ASME Section IX ASME Section VIII B31.1/B31.3 7 / 10A non-essential variable may be changes without re-qualification because: Nobody cares about non-essential variables The welder is allowed to change variables at his discretion Non-essential variables do not affect the mechanical or notch-toughness properties Non-essential variables cannot be changes without re-qualification 8 / 10Groove weld test may be used for qualification of welders. Which of the following shall be used for evaluation if welding process is SMAW? Only bend tests Only radiography Both radiography and bend tests Either bend tests or radiography None of the above 9 / 10Tension tests may be used in lieu of bend tests to qualify welders or welding operators. True False 10 / 10What period of inactivity from a given welding process requires the welder to re-qualify in that process? More than 3 months More than 6 months More than 4 months More than 12 months As stated by the AI (Authorized Inspector) Your score is LinkedIn Facebook VKontakte 0% Restart quiz Please rate this quiz Send feedback /10 1 votes, 5 avg 113 Created on March 09, 2023ASME Section IX Quiz-3ASME Section IX quiz one should take before interview 1 / 10May a welder, qualified in the 2G position on ¼ inch thick plate, can weld a 1 inch outside diameter pipe, ¼ inch thick in the horizontal position without re-qualification? Yes No Not enough information provided Yes, provided pipe is carbon steel, P#1 2 / 10A welding procedure must be qualified with impact tests only when required by the applicable construction code, such as ASME VIII Div.1 True False 3 / 10When using Macro-examination of fillet weld tests, the weld and the HAZ must not reveal cracks when magnified at No magnification is required – visual examination is required, only 5X 2X 10X 4 / 10Ferrous weld metal chemical composition may be designated using: F Number P Number A Number SFA Number Any of the Above 5 / 10A welder depositing 1/2" of weld metal with the SMAW process with 4 layers is qualified to deposit up to ____________ of weld metal. 8” Max to be welded 1” ½” All of the above 6 / 10May a welder who qualified using a double-groove weld, make a single V-groove weld without backing? Yes No Not enough information provided Yes, because backing is not an essential variable for a welder 7 / 10The maximum preheat temperature decrease allowed without re-qualification of a GMAW groove weld procedure is: 55 Degree Fahrenheit 55 Degree Celsius 50 Degree Fahrenheit No decrease in preheat is allowed as it is essential variable 8 / 10A variable that, when changed will cause a change in the mechanical properties of the weldment is called a: Essential variable Non-essential variable Supplementary essential variable All of the above 9 / 10Who is responsible for qualification of welding procedures, welders and welding operators? The Inspector The AI The Shop Foreman The Manufacturer of Contractor Any of the above 10 / 10The data recorded on a PQR (non-editorial) may be changed provided : The AI approves The test data on a PQR is a record of what occurred and should never be changed. Only editorial information can be changed on a PQR The API 510 inspector approves The date of the WPS is changed Your score is LinkedIn Facebook VKontakte 0% Restart quiz Please rate this quiz Send feedback /10 1 votes, 5 avg 106 Created on March 09, 2023ASME Section IX Quiz-4ASME Section IX quiz one should take before interview 1 / 10P No. for SA335 Gr. P91 is P5B P15F P15E P1 2 / 10Which of the following requires requalification of PQR if changed in production Essential variable Non-essential variable Supplementary essential variable if applicable A and C both 3 / 10PQR qualification for corrosion resistant overlay requires testing Only Bend Test Tensile and Bend only Chemical, PT , Bend Only Chemical, PT , Tensile, Hardness and Bend Only 4 / 10Welder can be qualified with volumetric NDE in lieu of bend test required, the minimum testing length required for volumetric NDE is 150mm 250mm 1 mtr No minimum Requirement 5 / 10The minimum and maximum base metal thickness qualified if PQR of material SA312 TP 304L(P8) is qualified with base metal thickness 18mm and impact test is required in job 1.5 to 36mm 5 to 36mm 16 to 36mm 18 to 36mm None of the above 6 / 10Which of the following is a essential variable for qualification of welding operator P Number Base Metal Thickness Diameter All of the above None of the above 7 / 10Which of the following is non-essential variable for PQR qualification for GTAW welding process PWHT Use of Thermal Processes Heat Input Consumable Insert 8 / 10Welder Qualified for corrosion resistant overlay on 10 mm thick base metal can weld on Any Thickness 10mm and Below 10mm and above 20mm and below 9 / 10A Welder qualified on plate with groove weld test assembly in 3g Position is also qualified to weld on pipe in All positions above 73mm diameter F and vertical over 73mm to 610mm diameter F over 73mm to 610mm diameter F in all diameters 10 / 10Ultrasonic Examination for qualification of welders can be conducted on thickness over 12mm 6mm Any Thickness Welder can not be qualified with Ultrasonic testing Your score is LinkedIn Facebook VKontakte 0% Restart quiz Please rate this quiz Send feedback